05CuPCrNi material will fluctuate within a narrow range

Tempering the important 05CUPCRNI material welding structure often use high temperature tempering to remove residual weld stress. Classification: high temperature tempering above 400 ℃, medium temperature tempering 250 ~ 400 ℃, low temperature tempering 150 ~ 250 ℃, Quenching +Tempering is improve 05CUPCRNI material strength, plasticity and toughness.

The mechanical properties of 20MnV steel are as follows: tensile strength 785 MPa, yield strength 590 MPa, elongation after fracture 10%, reduction of area 40%, impact absorption energy 55 J. 05CUPCRNI material, 20MnV steel has good properties, good strength, toughness and plasticity, good hardenability and machinability. After carburizing, 20MnV steel can be directly quenched without secondary quenching to improve the core structure. The weldability of 20MnV steel is good, but there is temper brittleness at 300-360 ℃ during heat treatment.

For ASTM A573 Grade 70/A573 Gr.70 carbon manganese silicon steel plates, our company would issue the original mill test certificate 05CUPCRNI material EN 10204 3.1 for clients when arrange delivery, so that clients can trace the A573 Gr.70 plates origin easily.

We had a wonderful trip in Phuket Island, Thailand. At the end of 2019, in order to thank employees for their hard work for a year and enrich their lives, our company organized a pleasant trip to Phuket Island, Thailand. The tour lasted 6 days and 5 nights, and returned by plane on the evening of December 27. We took off in Zhengzhou at about 5 o'clock in the afternoon on the 22th December.