cold rolled 05CuPCrNi high strength low alloy steel

According to the latest statistics of alacero, the consumption of finished steel cold rolled 05CUPCRNI products in Latin America in 2019 was 64.2 million tons, down 5% from 67.6 million tons in 2018. The decline in steel consumption in the region reflects the economic contraction of Latin American countries, especially the three major economies: Mexico, Argentina and Brazil. The three countries accounted for 87% of the total reduction in cold rolled 05CUPCRNI steel consumption in Latin America. Alacero said the main reasons for the decline in steel consumption in the region are the global economic slowdown, the fall in commodity prices, trade disputes between the United States and its partners, the shrinking world trade cold rolled 05CUPCRNI and political uncertainty, as well as the negative impact on Latin American countries and their neighbors in terms of investment.

Composition characteristics of low alloy structural steel, cold rolled 05CUPCRNI: (1) Low carbon: the carbon content of low alloy structural steel is less than 0.20% due to the high requirements of toughness, weldability and cold formability. (2) The alloy elements such as manganese are added. (3) The addition of Nb, Ti or V and other auxiliary elements: a small amount of Nb, Ti or V forms fine carbides or carbonitrides in the steel, which is beneficial to obtain fine ferrite grains and improve the strength and toughness of low alloy structural steel. In addition, adding a small amount of copper (≤ 0.4%) and phosphorus (about 0.1%) can improve the corrosion resistance. The addition of a small amount of rare earth elements can remove sulfur and gas, purify the steel, and improve the toughness and process performance of low alloy structural steel.

A514 grade R high strength structural steel chemical composition (melting analysis)%C: 0.15-0.20, Si: 0.20-0.35, Mn: 0.85-1.15, P max.: 0.035, S max.: 0.035, B max.: 0.005, Cr: 0.40-0.65, Ni: 0.90-1.10, Mo: 0.15-0.25, V: 0.03-0.08The mechanical properties in thickness (mm)T≤65Yield strength (≥Mpa): 690Tensile strength (Mpa):760-895Elongation in ≥,%: 18

"Adhere to green development, implement basic national policies to conserve resources and protect the environment, and take the goal of creating a resource-saving and environment-friendly iron and steel joint enterprise to promote the construction of ecological civilization.Strengthen the construction of core talents, further release the talents' innovative wisdom and innovation potential, and promote the efficient and high-quality development of enterprises. Adhere to the people-oriented principle, persist in relying on employees for development, share development results with employees, and build a harmonious enterprise."