High quality grade 09CuPCrNi-B manufacturer in China

The company covers an area of 15,000 square meters and the plant construction area is 10,000 square meters. We have introduced more than 50 sets of advanced grade 09CUPCRNI-B production equipment, auxiliary equipment and testing equipment at home and abroad, more than 260 employees, more than 20 middle and senior management staff, more than 10 professional and technical personnel, annual production capacity of 100,000 tons. Main products: flat steel, grade 09CUPCRNI-B steel pipe, steel plate, section steel, steel structure processing parts, etc. We also accept incoming materials and annealing processing.

A516Gr.65material is a carbon steel plate for medium and low temperature pressure vessels, which implements the ASTM A516 standard of the American Standard. The grade 09CUPCRNI-B) product minimum thickness that can be provided is 8mm and the width is 1500~4000mm. It has sufficient strength and toughness, good welding performance and hot and cold processing performance. A516Gr.65 steel plate can be used to manufacture pressure vessel steel for petrochemical, gas separation and gas storage, oil storage tank and transportation equipment.

The difference between cold rolled steel sheet and hot rolled steel plate. The carbon content of grade 09CUPCRNI-B, hot rolled steel plate is slightly higher than that of cold rolled steel sheet. In the case of little difference in composition, the density of cold rolled steel sheet and hot rolled steel plate is the same. Hot rolled steel plate has characteristics of low hardness, easy processing and good ductility. Cold rolled steel sheet has high hardness, and it is relatively difficult for processing. But it is not easy to deform and has high strength. Hot rolled steel plate can be made into alloy steel plate by adding other elements, and its properties are also excellent compared with other high-quality steel plates.

S355J2 steel plate rolling process is controlled rolling process. In the rolling process, the ingot rolling temperature is 1000-1050℃; in the first stage, the low-speed and large reduction rolling process is adopted, the high-temperature stage is 950-1000℃, the grade 09CUPCRNI-B rolling speed is 1.6-2.0m/s, the single reduction rate is 15-20%, and the cumulative reduction rate is 40-45%, so as to ensure sufficient deformation of ingot. In the first stage, the start rolling temperature is 910-930℃, and the finish rolling temperature is ≤ 870℃.As a basic building material, steel plates are currently widely used in automobiles, shipbuilding, chemical industry, aerospace and other fields. Reasonable selection of flaw detection methods to ensure the quality of grade 09CUPCRNI-B steel plates is of great significance to safe production. Common defects of steel plates are folding, inclusion, shrinkage, air bubbles, delamination and cracks. These problems can be discovered in time through flaw detection.

Heat treatment specification and microstructure of grade 09CUPCRNI-B, 12Cr1MoV alloy plate:Heat treatment specification: quenching 970 ℃, air cooling; tempering 750 ℃, air cooling. Microstructure: bainite + ferrite.Mechanical properties of 12Cr1MoV alloy plate:Tensile strength σb (MPa)：≥490(50); Yield strength σs (MPa)：≥245(25); Elongation δ5 (％)：≥22; area shrinkage ψ (%): ≥ 50; Impact energy Akv (J): ≥ 71; Impact toughness value αkv (J/cm2)：≥88(9).

After sales service support personnel pay attention to commitment in their work. In the process of people to people communication, mutual trust is an important factor for the long-term and stable communication. After sales service personnel must do what they say in the process of communication with customers.