Russian steel manufacturers increase quotation of 09cupcrni-a steel

09cupcrni-a steel 2020 stock in Shanghai: 25*1600*9300, 23.1*2590*7790, 25*1600*9300, 25*1600*9500, 14*1950*10800, 25*1600*9500, 20*1400*11400, 30*1600*8600, 30*2000*10200, 14*1950*10950, 25*1600*9300, 30*1600*8600, 9*2300*6870, 35*2500*9000, 9*2300*6870, 25*1600*9500, 9*2300*6870, 6*2000*10000, 20*1640*11250, 70*2270*7900, 6*2000*10000, 30*1600*8600.

X-rays or γ-rays are projected on the surface of the steel plate, and rubber can be placed on the other side of the steel plate. Since the radiation propagates through the steel plate and is absorbed, the intensity is different due to the presence or absence of defects, so the film can record the shape and position of the defects. This 09cupcrni-a steel method is sensitive to the detection of common steel plate defects such as slag inclusions, porosity and pores. The disadvantage is that it is difficult to find the specific depth of the defect and it is not easy to find cracks.

Vanadium mainly exists in the form of carbide in 09cupcrni-a steel and so on steel. Its main function is to refine the structure and grain size of steel and reduce the strength and toughness of steel. When the solid solution is dissolved at high temperature, the hardenability is increased; conversely, if it is in the form of carbide, the hardenability is reduced. Vanadium increases the tempering stability of quenched steel and produces secondary hardening effect. The vanadium content in steel, except high speed tool steel, is generally less than 0.5%.

After adding trace elements such as phosphorus, copper, chromium, and nickel to Q355NH steel, a dense and highly adherent protective film is formed on the surface of the weathering steel, which prevents rust from spreading and developing, and protects the substrate under the rust layer to slow its corrosion . An amorphous spinel oxide layer of about 50 μm to 100 μm thick formed between the rust layer and the substrate is dense and has good adhesion to the base metal, which greatly improves the atmospheric corrosion resistance of the steel material, 09cupcrni-a steel.